Fast-Curing Tgic Polyester Resin for Coating Applications Fx-D903

• Customization: Available
• CAS No.: 25135-73-3
• Formula: C22h26o10
• Model NO.: FX-D903
• EINECS: N/a
• Color: White
• Type: Powder Coating Resins
• Application: Powder Coating
• Characteristic: Good Adhesion, Good Weather Resistance
• Tg: Greater Than or Equal to 62
• Acid Value: 30-35mgkoh/G
• Viscosity: 4500-5500cps
• Curing Conditions: 200ºC/10min
• Product Appearance: White Particles
• Resin/Tgic: 93/7
• Transport Package: PE Bag
• Specification: 25KG/Bag
• Trademark: AquaCity
• Origin: China
• HS Code: 3907999990
• Production Capacity: 15000tons/Year
• Package Size: 53.00cm * 39.00cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

Product Parameters

Curing Agent	Triglycidyl Isocyanurate(TGIC)
	Hydroxy alkyl amide(HAA)
Type of Resins		Item No.	Ratio PE/Crosslinker	Acid Value (mgKOH/g)	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Cure cycle ºC/min	Key Features
TGIC Based Polyester Resins		FX-D902	93/7	30~35	4000~5000	≥64	200*10	High gloss ,Excellent flow, weathering resistance and mechanical properties
		FX-D903	93/7	30~35	4500~5500	≥62	200*10	Super weathering resistance, Excellent mechanical properties,good flow
		FX-D906	93/7	30~35	4000~5000	≥65	200*10	High gloss ,Excellent flow, boiling water resistance, mechanical properties
		FX-D907	93/7	29~35	5000~6000	≥67	200*10	Good weathering resistance and mechanical properties,,suitable for texture powder coating
		FX-D801	96/4	18~24	5500~6500	≥65	200*10	For dry blend matte system as fast component,good storage stability
		FX-D802	93/7	30~36	3800~4800	≥65	200*10	Excellent flow,suitable for High gloss and matt
		FX-D808	90/10	48~55	2800~3800	≥66	200*10	For dry blend matte system as fast component,good storage stability
		FX-D301	96/4	18~24	5000~6000	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
		FX-D303	93/7	30~36	3600~4600	≥64	200*10	Low cost resin,good flow and mechanical properties
		FX-D307	93/7	30~35	4800~6000	≥65	200*10	Low cost resin,suitable for texture powder coating
		FX-D308	90/10	50~56	2600~3600	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
Primid(HAA) Based Polyester Resins		FX-H602	95/5	20~25	4000~5000	≥64	180*15	Low cost resin,good flow and mechanical properties
		FX-H604	96.5/3.5	18~24	6000~7500	≥61	180*15 200*10	Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing

AQUACITY FX-D903 

Product Name			Powder Coating Polyester Resin
Product Model			FX-D903
Product Description			FX-D903 is a 93/7, TGIC curing powder coating special carboxyl terminated super weather resistant polyester resin for curing at 200 ºC. FX-D903 breaks through the characteristics of poor impact performance of traditional super weather resistant resin, and has excellent mechanical properties, leveling and impact properties. It is widely used in aluminum profile powder
Product appearance			White particles
Viscosity (200 ° C,mpa.s)			4500~5500
Acid Value(mgKOH/g)			30~35
Glass Transition  Temperature			≥62
Curing Ratio			93/7

EXTRUSION AND  APPLICATION CONDITIONS

Squeeze
Screw			40HZ
Zone 1 temperature			100
Zone 2  temperature			110
Application
Film thickness, substrate			60-80um film thickness, 0.5mm cold rolled steel plate
Gloss			≥90%
Recoil(kg.cm)			50
Foreflush(kg.cm)			50
Adhesion(grade)			0

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 

• Storage temperature <= 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.