Tgic Polyester Resin for Textured Powder Coatings Carboxyl Saturation

• CAS No.: 25135-73-3
• Formula: C22h26o10
• Color: White
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: FX-B307
• Type: Powder Coating Resins
• Application: Powder Coating
• Characteristic: Good Adhesion,Good Weather Resistance
• Tg: Greater Than or Equal to 65
• Acid Value: 30-35mgkoh/G
• Viscosity: 4800-6000cps
• Curing Conditions: 200ºC/10min
• Product Appearance: White Particles
• Resin/Tgic: 93/7
• Transport Package: PE Bag
• Specification: 25KG/Bag
• Trademark: AquaCity
• Origin: China
• HS Code: 3907999990
• Production Capacity: 15000tons/Year
• Package Size: 53.00cm * 39.00cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

Curing Agent	Triglycidyl Isocyanurate(TGIC)
	Hydroxy alkyl amide(HAA)
Type of Resins		Item No.	Ratio PE/Crosslinker	Acid Value (mgKOH/g)	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Cure cycle ºC/min	Key Features
TGIC Based Polyester Resins		FX-B902	93/7	30~35	4000~5000	≥64	200*10	High gloss ,Excellent flow, weathering resistance and mechanical properties
		FX-B903	93/7	30~35	4500~5500	≥62	200*10	Super weathering resistance, Excellent mechanical properties,good flow
		FX-B906	93/7	30~35	4000~5000	≥65	200*10	High gloss ,Excellent flow, boiling water resistance, mechanical properties
		FX-B907	93/7	29~35	5000~6000	≥67	200*10	Good weathering resistance and mechanical properties,,suitable for texture powder coating
		FX-B801	96/4	18~24	5500~6500	≥65	200*10	For dry blend matte system as fast component,good storage stability
		FX-B802	93/7	30~36	3800~4800	≥65	200*10	Excellent flow,suitable for High gloss and matt
		FX-B808	90/10	48~55	2800~3800	≥66	200*10	For dry blend matte system as fast component,good storage stability
		FX-B301	96/4	18~24	5000~6000	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
		FX-B303	93/7	30~36	3600~4600	≥64	200*10	Low cost resin,good flow and mechanical properties
		FX-B307	93/7	30~35	4800~6000	≥65	200*10	Low cost resin,suitable for texture powder coating
		FX-B308	90/10	50~56	2600~3600	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
Primid(HAA) Based Polyester Resins		FX-H602	95/5	20~25	4000~5000	≥64	180*15	Low cost resin,good flow and mechanical properties
		FX-H604	96.5/3.5	18~24	6000~7500	≥61	180*15 200*10	Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing

AQUACITY FX-B307

Product Name			Powder Coating Polyester Resin
Product Model			FX-B307
Product Discription			FX-B307 is a special carboxyl terminated polyester resin for HAA and TGIC double curing powder coatings at 200 ºC. FX-B307 resin is used for general industrial sand grain and orange grain paint. It has good weather resistance, excellent boiling performance and mechanical properties, and can significantly reduce the formulation cost when combined with HAA
Product appearance			White particles
Viscosity (200 ° C,mpa.s)			4800~6000
Acid Value(mgKOH/g)			30-35
Glass Transition  Temperature			≥65

APPLY THE INITIAL FORMULA

Components			Net  Wight
FX-B307			558
TGIC			42
Titanium Dioxide			300
Barium Sulfate			90
Swelling Figure			5
Sand grain agent			5

EXTRUSION AND  APPLICATION CONDITIONS

Squeeze
Screw			40HZ
Zone 1 temperature			100
Zone 2  temperature			110
Application
Film thickness, substrate			60-80um film thickness, 0.5mm cold rolled steel plate
Gloss			≥90%
Recoil(kg.cm)			50
Foreflush(kg.cm)			50
Adhesion(grade)			0

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION

• Storage temperature ≤ 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.