Powder Coating Resins for Architectural Interior and Exterior Applications F808

• Customization: Available
• CAS No.: 25135-73-3
• Formula: C22h26o10
• Model NO.: F808
• Color: White
• Type: Powder Coating Resins
• Application: Powder Coating
• Characteristic: Good Adhesion,Good Weather Resistance
• Tg: Greater Than or Equal to 66
• Acid Value: 48-55mgkoh/G
• Viscosity: 2800-3800cps
• Curing Conditions: 200ºC/10min
• Product Appearance: White Particles
• Resin/Tgic: 90/10
• Transport Package: One Ton /Pallet
• Specification: 25KG/bag
• Trademark: AQUACITY
• Origin: China
• HS Code: 3907999990
• Production Capacity: 15000tons/Year
• Package Size: 53.00cm * 39.00cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

Curing Agent	Triglycidyl Isocyanurate(TGIC)
	Hydroxy alkyl amide(HAA)
Type of Resins		Item No.	Ratio PE/Crosslinker	Acid Value (mgKOH/g)	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Cure cycle ºC/min	Key Features
TGIC Based Polyester Resins		F902	93/7	30~35	4000~5000	≥64	200*10	High gloss ,Excellent flow, weathering resistance and mechanical properties
		F903	93/7	30~35	4500~5500	≥62	200*10	Super weathering resistance, Excellent mechanical properties,good flow
		F906	93/7	30~35	4000~5000	≥65	200*10	High gloss ,Excellent flow, boiling water resistance, mechanical properties
		F907	93/7	29~35	5000~6000	≥67	200*10	Good weathering resistance and mechanical properties,,suitable for texture powder coating
		F801	96/4	18~24	5500~6500	≥65	200*10	For dry blend matte system as fast component,good storage stability
		F802	93/7	30~36	3800~4800	≥65	200*10	Excellent flow,suitable for High gloss and matt
		F808	90/10	48~55	2800~3800	≥66	200*10	For dry blend matte system as fast component,good storage stability
		F301	96/4	18~24	5000~6000	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
		F303	93/7	30~36	3600~4600	≥64	200*10	Low cost resin,good flow and mechanical properties
		F307	93/7	30~35	4800~6000	≥65	200*10	Low cost resin,suitable for texture powder coating
		F308	90/10	50~56	2600~3600	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
Primid(HAA) Based Polyester Resins		H602	95/5	20~25	4000~5000	≥64	180*15	Low cost resin,good flow and mechanical properties
		H604	96.5/3.5	18~24	6000~7500	≥61	180*15 200*10	Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing

AQUACITY F808

Product Name			Powder Coating Polyester Resin
Product Model			F808
Product Description			F808 is high and low acid value polyester resin. For polyester/TGIC curing powder coating system. After being made into powder by F808, it can be dry mixed to make outdoor semi gloss powder coating, which has low luster, good weather resistance and leveling property.
Product appearance			White particles
Viscosity (200 ° C,mpa.s)			2800~3800
Acid Value(mgKOH/g)			48-55
Glass Transition  Temperature			≥66
Curing Ratio			90/10

APPLY THE INITIAL FORMULA

Components			Net  Wight
F808			540
TGIC			60
Titanium Dioxide			200
Barium Sulfate			177
Flatting Agent			10
Brightener			10
Benzoin			3

EXTRUSION AND  APPLICATION CONDITIONS

Squeeze
Screw			40HZ
Zone 1 temperature			105
Zone 2  temperature			110
Application
Film thickness, substrate			60-80um film thickness, 0.5mm cold rolled steel plate
Gloss			<25%
Recoil(kg.cm)			50
Foreflush(kg.cm)			50
Adhesion(grade)			0

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION

• Storage temperature ≤ 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.