Hydroxyl Acrylic Dispersion Water-Based Resin-2145

• Application: Top-Coat Paint on Steelstructure, Plastic Varnish
• Appearance: Milky White Liquid
• Solid Wt %: 45±2
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: 2145
• Viscosity (MPa.S): 300-3000
• pH Value: 7.0-9.0
• Hydroxyl Content: 4.2
• Mfft / ºC: 40
• Transport Package: 200kg/Drum
• Specification: 200kg/Drum
• Trademark: AquaCity
• Origin: China
• Production Capacity: 5000tons
• Package Size: 58.00cm * 58.00cm * 98.00cm
• Package Gross Weight: 200.000kg

Product Description

FX-2145

Product Introduction

Resin Type

:

Orthophthalic

It can be used with polyurethane curing agent or amino resin to prepare water-based amino baking paint and two-component low-temperature/self-drying water-based paint with excellent performance. It has excellent performance and good appearance

Major Features

:

• Gloss >= 90°,Adhension<=Grade 1,hardness>=2H.
• Excellent fullness
• Good chemical resistance
• Good effect on silver powder orientation arrangement

Application

:

metal paint, wood paint, plastic, ink, printing paste

Product Technical Parameter

:

Liquid Resin	Parameters	Unit	Testing Standard
Appearance	Milky white liquid	-	Visual Inspection
Viscosity (25ºC, 20r)	300-3000	mPa·s	GB/T 7193
PH value	7-9	-	FT/JZ208
MFFT/ °C	40	mgKOH/g	GB/T 7193
Hydroxyl content	4.2	%	GB/T 7193
Solid ±1%	45	min	GB/T 7193
Cured Property	Parameters	Unit	Testing Standard
Tensile Strength	60	MPa	GB/T 2567
Tensile Modulus	3300	MPa	GB/T 2567
Flexural Strength	131	MPa	GB/T 2567
Flexural Modulus	3700	MPa	GB/T 2567
Barcol Hardness	46	-	GB/T 3854
Heat Deflection Temperature	70	ºC	GB/T 1634

Package

:

125ml/drum

Storage

:

• Store in an airtight container at 5-35ºC
• Storage time 6 months
• Avoid freezing and high temperature

Disclaimer:
The information contained in this technical instruction is real and for users' consideration and test reference only. In the view of actual conditions of usage, storage and handling are being totally beyond our control, customer should evaluate the data and product and make their own tests to determine the suitability of our product for their respective use in full scale production for his own purpose and under his operating conditions.