| Customization: | Available |
|---|---|
| CAS No.: | 25135-73-3 |
| Formula: | C22h26o10 |
|
Still deciding? Get samples of US$ 1.8/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Curing Agent | Triglycidyl Isocyanurate(TGIC) | |||||||
| Triglycidyl Isocyanurate(TGIC)&Hydroxy alkyl amide(HAA) | ||||||||
| Hydroxy alkyl amide(HAA) | ||||||||
| Type of Resins | Item No. | Ratio PE/Crosslinker |
Acid Value (mgKOH/g) |
Viscosity(p/200ºC) /mpa.s |
Tg Value (°C) |
Cure cycle ºC/min |
Key Features | |
| TGIC Based Polyester Resins | FX-I902 | 93/7 | 30~35 | 3600~4600 | ≥66 | 200*10 | High gloss ,Excellent flow, weathering resistance and mechanical properties | |
| FX-I903 | 93/7 | 32~36 | 4000~5000 | ≥62 | 200*10 | Super weathering resistance, Excellent mechanical properties,good flow | ||
| FX-I906 | 93/7 | 30~35 | 4000~5000 | ≥65 | 200*10 | High gloss ,Excellent flow, boiling water resistance, mechanical properties | ||
| FX-I907 | 93/7 | 29~35 | 5000~6000 | ≥67 | 200*10 | Good weathering resistance and mechanical properties,,suitable for texture powder coating | ||
| FX-I801 | 96/4 | 18~24 | 4800~6000 | ≥65 | 200*12 | For dry blend matte system as fast component,good storage stability | ||
| FX-I802 | 93/7 | 30~36 | 3800~4800 | ≥65 | 200*10 | Excellent flow,suitable for High gloss and matt | ||
| FX-I808 | 90/10 | 50~55 | 2800~3600 | ≥65 | 200*12 | For dry blend matte system as fast component,good storage stability | ||
| FX-I301 | 96/4 | 18~24 | 4800~6000 | ≥65 | 200*12 | Low cost resin,for dry blend matte system as fast component,good storage stability |
||
| FX-I303 | 93/7 | 28~35 | 3000~4000 | ≥64 | 200*10 | Low cost resin,good flow and mechanical properties | ||
| FX-I307 | 93/7 | 28~35 | 5000~6000 | ≥66 | 200*10 | Low cost resin,suitable for texture powder coating | ||
| FX-I308 | 90/10 | 50~55 | 2800~3500 | ≥65 | 200*12 | Low cost resin,for dry blend matte system as fast component,good storage stability |
||
| TGIC and HAA Based Polyester Resins | FX-I288 | TGIC:94/6 HAA:95/5 |
28~33 | 3600~4600 | ≥62 | 200*10 | Special carboxyl terminated polyester resin for TGIC and HAA dual curing powder coatings, with good weather resistance, boiling resistance, high gloss and easy extinction | |
| Primid(HAA) Based Polyester Resins | FX-H602 | 95/5 | 20~25 | 4000~5000 | ≥64 | 180*15 | Low cost resin,good flow and mechanical properties | |
| FX-H604 | 96.5/3.5 | 18~24 | 6000~7500 | ≥61 | 180*15 200*10 |
Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing | ||
| Product Name | Powder Coating Polyester Resin | ||||
| Product Model | FX-I288 | ||||
| Product Description | FX-I288 is a special carboxyl terminated polyester resin for 94/6 economical TGIC and HAA dual curing powder coatings cured at 200 ºC. FX-I288 resin is used for outdoor decorative powder paint, which has good weather resistance, boiling resistance, high luster and easy extinction | ||||
| Product appearance | White particles | ||||
| Viscosity (200 ° C,mpa.s) | 3600~4600 | ||||
| Acid Value(mgKOH/g) | 28-33 | ||||
| Glass Transition Temperature | ≥62 | ||||
| Curing Ratio | TGIC:94/6 HAA:95/5 |
| Squeeze | |||||||
| Screw | 40HZ | ||||||
| Zone 1 temperature | 100 | ||||||
| Zone 2 temperature | 110 | ||||||
| Application | |||||||
| Film thickness, substrate | 60-80um film thickness, 0.5mm cold rolled steel plate | ||||||
| Gloss | ≥90% | ||||||
| Recoil(kg.cm) | 50 | ||||||
| Foreflush(kg.cm) | 50 | ||||||
| Adhesion(grade) | 0 | ||||||
| Foshan Faxus New Material Company Limited |
| Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties. |