CAS No.: | 25135-73-3 |
---|---|
Formula: | C22h26o10 |
Color: | White |
Samples: |
White Solids Granular
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Curing Agent | Triglycidyl Isocyanurate(TGIC) | |||||||
Hydroxy alkyl amide(HAA) | ||||||||
Item No. | Ratio PE/Crosslinker |
Acid Value (mgKOH/g) |
Viscosity(p/200ºC) /mpa.s |
Tg Value (°C) |
Cure cycle ºC/min |
Key Features | ||
Outdoor polyester resins for powder coatings | TGIC based polyester resins | C902 | 93/7 | 30~35 | 4000~5000 | ≥64 | 200*10 | High gloss ,Excellent flow, weathering resistance and mechanical properties |
C903 | 93/7 | 30~35 | 4500~5500 | ≥62 | 200*10 | Super weathering resistance, Excellent mechanical properties,good flow | ||
C906 | 93/7 | 30~35 | 4000~5000 | ≥65 | 200*10 | High gloss ,Excellent flow, boiling water resistance, mechanical properties | ||
C907 | 93/7 | 29~35 | 5000~6000 | ≥67 | 200*10 | Good weathering resistance and mechanical properties,,suitable for texture powder coating | ||
C801 | 96/4 | 18~24 | 5500~6500 | ≥65 | 200*10 | For dry blend matte system as fast component,good storage stability | ||
C802 | 93/7 | 30~36 | 3800~4800 | ≥65 | 200*10 | Excellent flow,suitable for High gloss and matt | ||
C808 | 90/10 | 48~55 | 2800~3800 | ≥66 | 200*10 | For dry blend matte system as fast component,good storage stability | ||
C301 | 96/4 | 18~24 | 5000~6000 | ≥65 | 200*10 | Low cost resin,for dry blend matte system as fast component,good storage stability |
||
C303 | 93/7 | 30~36 | 3600~4600 | ≥64 | 200*10 | Low cost resin,good flow and mechanical properties | ||
C307 | 93/7 | 30~35 | 4800~6000 | ≥65 | 200*10 | Low cost resin,suitable for texture powder coating | ||
C308 | 90/10 | 50~56 | 2600~3600 | ≥65 | 200*10 | Low cost resin,for dry blend matte system as fast component,good storage stability |
||
Primid(HAA) based polyester resins | H602 | 95/5 | 20~25 | 4000~5000 | ≥64 | 180*15 | Low cost resin,good flow and mechanical properties | |
H604 | 96.5/3.5 | 18~24 | 6000~7500 | ≥61 | 180*15 200*10 |
Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing |
Model | Mg KOH/g | Viscosity(mPa.s) | Tg | TGIC | Building material grade (IDTY) | ||
C-903 | 30~35 | 4500~5500 | ≥62 | 7/93 | American Standard aama2605 weather resistance standard | ||
Products | Brand | Market and Application | Final Product Advantages | Product appearance | Nature and Chemistry | Model | Product Discription |
Outstanding weather resistant TGIC polyester resins for interior and exterior powder coating applications | AquaCity | Powder coating resins for aluminum | Outstanding weathering resistance | White | Saturated polyester resins | C-903 | C903 is a carboxyl functional polyester resin for use with 7% TGIC in the production of powder coatings. Formulations exhibit good flow and excellent outdoor durability. |
Powder coating resins for architectural interior and exterior applications | Great leveling surface | Solids | Thermosetting polyester resins | ||||
Powder coating for metals | Supper good machanical impact testing results | Granular | TGIC powder coating resns | ||||
Paint and coatings for Coil & Pre-Coated Metal | Excellent outdoor durability | Low/zero VOC | |||||
Paint and coatings for industrial Metals | Apply to High gloss and Matte surface effects |
Squeeze | |||||||
Screw | 40HZ | ||||||
Zone 1 temperature | 100 | ||||||
Zone 2 temperature | 110 | ||||||
Application | |||||||
Film thickness, substrate | 60-80um film thickness, 0.5mm cold rolled steel plate | ||||||
Gloss | ≥90% | ||||||
Recoil(kg.cm) | 50 | ||||||
Foreflush(kg.cm) | 50 | ||||||
Adhesion(grade) | 0 |
Foshan Faxus New Material Company Limited |
Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties. |
Suppliers with verified business licenses