B313 Low/Zero Voc Great Weather Resistant Tgic Polyester Resins Thermosetting Metal Finishing

• Customization: Available
• CAS No.: 25135-73-3
• Formula: C22h26o10
• Model NO.: B313
• EINECS: N/a
• Color: White
• Type: Tgic Powder Coating Resins
• Application: Powder Coating
• Tg: Greater Than or Equal to 62
• Acid Value: 28-35mgkoh/G
• Viscosity: 2500~3500cps
• Curing Conditions: 200ºC/10min
• Product Appearance: White Particles
• Resin/Tgic: 93/7
• Transport Package: One Ton /Pallet
• Specification: 25KG/bag
• Trademark: AQUACITY
• Origin: China
• HS Code: 3907999990
• Production Capacity: 15000tons/Year
• Package Size: 53.00cm * 39.00cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

Product Parameters

 

Curing Agent	Triglycidyl Isocyanurate(TGIC)
	Hydroxy alkyl amide(HAA)
Type of Resins		Item No.	Ratio PE/Crosslinker	Acid Value (mgKOH/g)	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Cure cycle ºC/min	Key Features
TGIC Based Polyester Resins		B902	93/7	30~35	4000~5000	≥64	200*10	High gloss ,Excellent flow, weathering resistance and mechanical properties
		B903	93/7	30~35	4500~5500	≥62	200*10	Super weathering resistance, Excellent mechanical properties,good flow
		B906	93/7	30~35	4000~5000	≥65	200*10	High gloss ,Excellent flow, boiling water resistance, mechanical properties
		B907	93/7	29~35	5000~6000	≥67	200*10	Good weathering resistance and mechanical properties,,suitable for texture powder coating
		B801	96/4	18~24	5500~6500	≥65	200*10	For dry blend matte system as fast component,good storage stability
		B802	93/7	30~36	3800~4800	≥65	200*10	Excellent flow,suitable for High gloss and matt
		B808	90/10	48~55	2800~3800	≥66	200*10	For dry blend matte system as fast component,good storage stability
		B301	96/4	18~24	5000~6000	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
		B303	93/7	30~36	3600~4600	≥64	200*10	Low cost resin,good flow and mechanical properties
		B313	93/7	28~35	2500-3500	≥62	200*10	Low cost resin, with good weather resistance and leveling property
		B307	93/7	30~35	4800~6000	≥65	200*10	Low cost resin,suitable for texture powder coating
		B308	90/10	50~56	2600~3600	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
Primid(HAA) Based Polyester Resins		H602	95/5	20~25	4000~5000	≥64	180*15	Low cost resin,good flow and mechanical properties
		H604	96.5/3.5	18~24	6000~7500	≥61	180*15 200*10	Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing

AQUACITY B313

Product Name			Powder Coating Polyester Resin
Product Model			B313
Product Description			B313 is a special carboxyl terminated polyester resin for 93/7 economical TGIC curing powder coating cured at 200 ºC. It has good weather resistance, leveling property, high gloss and easy extinction.it is applied to Paint and coatings for Coil & Pre-Coated Metal,Paint and coatings for industrial Metals
Product appearance			White particles
Viscosity (200 ° C,mpa.s)			2500~3500
Acid Value(mgKOH/g)			28-35
Glass Transition  Temperature			≥62
Curing Ratio			93/7

EXTRUSION AND  APPLICATION CONDITIONS

Squeeze
Screw			40HZ
Zone 1 temperature			100
Zone 2  temperature			110
Application
Film thickness, substrate			60-80um film thickness, 0.5mm cold rolled steel plate
Gloss			≥90%
Recoil(kg.cm)			50
Foreflush(kg.cm)			50
Adhesion(grade)			0

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 

• Storage temperature ≤ 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.