Tgic Polyester Resin with Excellent Weatherability for Outdoor Coatings Fx-F288

• CAS No.: 25135-73-3
• Formula: C22h26o10
• Color: White
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: FX-F288
• Type: Outdoor Powder Coating
• Application: Powder Coating
• Tg: Greater Than or Equal to 62
• Acid Value: 28-33mgkoh/G
• Viscosity: 3600-4600cps
• Curing Conditions: 200ºC/10min
• Product Appearance: White Particles
• Resin/Tgic: 94/6
• Resin/Haa: 95/5
• Transport Package: PE Bag
• Specification: 25KG/Bag
• Trademark: AquaCity
• Origin: China
• HS Code: 3907999990
• Production Capacity: 15000tons/Year
• Package Size: 53.00cm * 39.00cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

Curing Agent	Triglycidyl Isocyanurate(TGIC)
	Triglycidyl Isocyanurate(TGIC)&Hydroxy alkyl amide(HAA)
	Hydroxy alkyl amide(HAA)
Type of Resins		Item No.	Ratio PE/Crosslinker	Acid Value (mgKOH/g)	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Cure cycle ºC/min	Key Features
TGIC Based Polyester Resins		FX-F902	93/7	30~35	3600~4600	≥66	200*10	High gloss ,Excellent flow, weathering resistance and mechanical properties
		FX-F903	93/7	32~36	4000~5000	≥62	200*10	Super weathering resistance, Excellent mechanical properties,good flow
		FX-F906	93/7	30~35	4000~5000	≥65	200*10	High gloss ,Excellent flow, boiling water resistance, mechanical properties
		FX-F907	93/7	29~35	5000~6000	≥67	200*10	Good weathering resistance and mechanical properties,,suitable for texture powder coating
		FX-F801	96/4	18~24	4800~6000	≥65	200*12	For dry blend matte system as fast component,good storage stability
		FX-F802	93/7	30~36	3800~4800	≥65	200*10	Excellent flow,suitable for High gloss and matt
		FX-F808	90/10	50~55	2800~3600	≥65	200*12	For dry blend matte system as fast component,good storage stability
		FX-F301	96/4	18~24	4800~6000	≥65	200*12	Low cost resin,for dry blend matte system as fast component,good storage stability
		FX-F303	93/7	28~35	3000~4000	≥64	200*10	Low cost resin,good flow and mechanical properties
		FX-F307	93/7	28~35	5000~6000	≥66	200*10	Low cost resin,suitable for texture powder coating
		FX-F308	90/10	50~55	2800~3500	≥65	200*12	Low cost resin,for dry blend matte system as fast component,good storage stability
TGIC and HAA Based Polyester Resins		FX-F288	TGIC:94/6 HAA:95/5	28~33	3600~4600	≥62	200*10	Special carboxyl terminated polyester resin for TGIC and HAA dual curing powder coatings, with good weather resistance, boiling resistance, high gloss and easy extinction
Primid(HAA) Based Polyester Resins		FX-H602	95/5	20~25	4000~5000	≥64	180*15	Low cost resin,good flow and mechanical properties
		FX-H604	96.5/3.5	18~24	6000~7500	≥61	180*15 200*10	Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing

AQUACITY FX-F288 

Product Name			Powder Coating Polyester Resin
Product Model			FX-F288
Product Description			FX-F288 is a special carboxyl terminated polyester resin for 94/6 economical TGIC and HAA dual curing powder coatings cured at 200 ºC. FX-F288 resin is used for outdoor decorative powder paint, which has good weather resistance, boiling resistance, high luster and easy extinction
Product appearance			White particles
Viscosity (200 ° C,mpa.s)			3600~4600
Acid Value(mgKOH/g)			28-33
Glass Transition  Temperature			≥62
Curing Ratio			TGIC:94/6 HAA:95/5

APPLY THE INITIAL FORMULA

Components			Net  Wight
FX-F288			570
HAA			30
Titanium Dioxide			177
Barium Sulfate			200
Flatting Agent			10
Brightener			10
Benzoin			3

EXTRUSION AND  APPLICATION CONDITIONS

Squeeze
Screw			40HZ
Zone 1 temperature			100
Zone 2  temperature			110
Application
Film thickness, substrate			60-80um film thickness, 0.5mm cold rolled steel plate
Gloss			≥90%
Recoil(kg.cm)			50
Foreflush(kg.cm)			50
Adhesion(grade)			0

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 

• Storage temperature <= 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.