Metals Surface Protection Powder Coating for Architectural Metal Jsf001

• Customization: Available
• CAS No.: 113669-95-7
• Formula: N/a
• Model NO.: JSF001
• EINECS: 629-768-9
• Color: Customize
• Appearance: Powder
• Main Raw Material: Polyester Resin
• Method: Spray
• Level: Finish Coat
• Drying Method: Drying
• Certification: ISO14001, ISO9001, SGS
• Substrate: Steel & Aluminum & Metal
• Components: Film Forming Matter
• Formation Mechanism: Conversion Type
• Powder Coating: Smooth Powder Coating
• Application Tool: Electrostatic Spray Gun
• Curing Conditions: 160-200ºC10-15min
• Usage: Appliance Paint, Building Coating, Furniture
• Advantage: Environmental Friendly
• Brand Name: Kinno
• Transport Package: PP Bag + Carton Box
• Specification: 25KG/Carton
• Trademark: Kinno
• Origin: China
• HS Code: 3907999990
• Production Capacity: 10000tons/Year
• Package Size: 40.20cm * 29.70cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

 Metalic Paints And Powder Coatings System

Types	Item No.	Ratio PE/Crosslinker	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Coating film thickness(um)	Curing conditions
Matter Series  Powder Coating	JSX001	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Matte Series Powder Coating	JSP001	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Glossy Series Powder Coating	JSG001	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Matte Series Powder Coating	JSX001	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Fine Texture Matte Series Powder Coating	JSS001	93/7	4800~6000	≥65	40um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Rough Texture Glossy Series Powder Coating	JSZ001	93/7	4800~6000	≥65	40um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Flat Matte Series Powder Coating	JSF001	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min

 

 

Product Description

Physical And Chemical Properties
Flat coating film thickness	60um~80um
Curing conditions	160°C/20min; 180°C/15min; 200°C/12min
Acid value	30-36mgkOH/g
Glass transition temperature	≥65
Viscosity (200 ° C,mpa.s)	3800-4800mPa.s/200°C
Indentation hardness	≥80
Adhesion	Grade 0
Impact resistance	no cracking
Cupping test	6mm without cracking
Bending resistance	3mm without cracking
Chemical stability	no bubbles, softening, falling off
Salt spray corrosion resistance	R≤9.5
Moisture and heat resistance	≤ grade 1
Artificially accelerated weather resistance	level 0
Boiling water resistance	no bubbles, water spots, wrinkle spinning, falling off, slightly color difference allowed
Preparation method	After mixing the prepared polyester resin with curing agent TGIC, pigments, fillers and auxiliary agents according to the formula ratio, melt extrusion, tablet pressing and crushing with a twin-screw extruder, and then pulverize the sheet material and sieve it to make it. powder coating. It is sprayed on the surface-treated metal plate with an electrostatic spray gun.

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 

• Storage temperature ≤30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/carton or 20kg/carton, 1ton/pallet.

 