Waterborne Glass Baking Acrylic Resin for Flat Glass Paint

• Customization: Available
• Usage: Decorative Glass, Vessel Glass, and Flat Glass
• Color: Colorless to Yellow Transparent Liquid
• Model NO.: 1133-2
• Appearance: Liquid
• Method: Roller
• Main Raw Material: Acrylic Resin
• Level: Finish Coat
• Substrate: Glass
• Expiration Date: 1 year
• Packaging: Plastic Drum
• Storage and Transportation Temperature: 5ºC~40ºC
• Specification: 200kg/drum
• Trademark: Kinno
• Origin: China
• Production Capacity: 10000tons/Year
• Package Size: 10.00cm * 10.00cm * 70.00cm
• Package Gross Weight: 2.000kg

Product Description

Technical Data Sheet

Test items		Standard	Instruction
Hardness	H	≥3	High hardness and high gloss are the biggest characteristics
Gloss (60 °)	%	≥100
Adhesion	level	0	Can pass the 100 grid test and can be scraped with nails
Resistant to yellowing		but not yellowing
Water resistance		7 days	Normal temperature water, no abnormalities
Boiling water resistance (100 ºC)		60 minutes	Slight whitening after drying, no abnormalities after drying
Dishwasher resistance test	Times	5-15	To pass the dishwasher test, a sealant must be added
Salt spray resistance	H	No abnormalities within 96 hours
Acid resistance (5% HCL)	H	No abnormalities within 2 hours
Black paint density	Kg/L	1.35

Performance indicators: (Bake at 180 ºC for 20 minutes, test performance after 8 hours)

Disclaimer:
The information contained in this technical instruction is real and for users' consideration and test reference only. In the view of actual conditions of usage, storage and handling are being totally beyond our control, customer should evaluate the data and product and make their own tests to determine the suitability of our product for their respective use in full scale production for his own purpose and under his operating conditions.

Product performance and advantages:

1132 series adopts water-based acrylic resin and amino group, which are baked and cured at high temperatures (150 ºC~180 ºC) to form a film. The paint film has high gloss, high hardness, high scratch resistance, strong dry film adhesion, good water resistance, good acid and alkali resistance, and high cost-effectiveness. Multiple methods such as roller coating, spray coating, and spray coating can be used for construction. Suitable for various standard requirements such as decorative glass, vessel glass, and flat glass.

Precautions:

1. Cleaning glass: Before cleaning the glass, first mix the water paint with 10%, sealant 2%, and BL88%, and then clean the glass with a film washing machine. The surface of the glass should not have any residual cleaning solvent.

2. Roller coating or spray coating: Adjust the machine parameters reasonably according to the glass thickness and customer requirements.

3. Baking conditions: The temperature of the tunnel furnace is set at 180 ° C (actual furnace temperature), and the oven is baked for 15-20 minutes. The bread oven can be set between 120 ° -180 °, and the baking time is about 30 minutes.

4. Cooling conditions: Glass can be cooled at room temperature or with a fan, but remember not to use cold water to get wet and cool down. Glass must not overlap before cooling to room temperature to avoid scratching the glass paint surface.

5. Packaging and post-processing: Different packaging forms can be selected according to different industries, but regardless of the method, it is necessary to ensure that the water paint is fully dry and the glass is cooled; In the subsequent process, it is necessary to conduct corresponding tests (such as glue resistance, water boiling, heat resistance, etc.)