General Purpose Eco-Friendly Tgic Cured Electrostatic Powder Coating

• Customization: Available
• CAS No.: 113669-95-7
• Formula: N/a
• Model NO.: JWS01
• Usage: Aluminium Profiles,Steel and Other Metal Substrate
• Color: Customized
• Appearance: Powder
• Method: Spray
• Components: Film Forming Matter
• Main Raw Material: Polyester Resin
• Level: Finish Coat
• Certification: ISO14001, ISO9001, SGS
• Substrate: Aluminum
• Expiration Date: 6 Months
• Formation Mechanism: Conversion Type
• Packaging: Plastic Bag & Carton
• Powder Coating: Fine Textured Matte Powder
• Spraying Way: Electrostatic Coating
• Curing Agent: Tgic Hardener
• Advantage: Environmental Friendly
• Transport Package: Carton
• Specification: 25KG/carton
• Trademark: KINNO
• Origin: China
• HS Code: 3907999990
• Production Capacity: 10000tons/Year
• Package Size: 40.20cm * 29.70cm * 45.00cm
• Package Gross Weight: 25.000kg

Product Description

 Metalic Paints And Powder Coatings System

Types	Item No.	Ratio PE/Crosslinker	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Coating film thickness(um)	Curing conditions
Matter Series  Powder Coating	JWX01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Matte Series Powder Coating	JWP01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Glossy Series Powder Coating	JWG01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Matte Series Powder Coating	JWX01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Fine Texture Matte Series Powder Coating	JWS01	93/7	4800~6000	≥65	40um~80um	160°C/20min;180°C/15min ;200°C/12min
Metallic Rough Texture Glossy Series Powder Coating	JWZ01	93/7	4800~6000	≥65	40um~80um	160°C/20min;180°C/15min ;200°C/12min
Smooth Flat Matte Series Powder Coating	JWF01	93/7	3800~4800	≥65	60um~80um	160°C/20min;180°C/15min ;200°C/12min

 

 

Product Description

Physical And Chemical Properties
Sand grain coating film thickness	40u~80um
Curing conditions	160°C/20min;180°C/15min ;200°C/12min
Acid value	30-35mgKOH/g
Glass transition temperature	≥65
Viscosity (200 ° C,mpa.s)	4800-6000mPa.s/200ºC
Indentation hardness	≥80
Adhesion	Grade 0
Impact resistance	no cracking
Cupping test	6mm without cracking
Bending resistance	3mm without cracking
Chemical stability	no bubbles, softening, falling off
Salt spray corrosion resistance	R≤9.5
Moisture and heat resistance	≤ grade 1
Artificially accelerated weather resistance	level 0
Boiling water resistance	no bubbles, water spots, wrinkle spinning, falling off, slightly color difference allowed
Preparation method	After mixing the prepared polyester resin with curing agent TGIC, pigments, fillers and auxiliary agents according to the formula ratio, melt extrusion, tablet pressing and crushing with a twin-screw extruder, and then pulverize the sheet material and sieve it to make it. powder coating. It is sprayed on the surface-treated metal plate with an electrostatic spray gun.

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 

• Storage temperature <= 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/carton or 20kg/carton, 1ton/pallet.

 