Excellent Outdoor Durability Low/Zero Voc Polyester Resins J902

• Customization: Available
• CAS No.: 68551-15-5
• Formula: N/a
• Model NO.: J902
• EINECS: 609-946-4
• Molecular Principal Chain: Heterochain Polymer
• Color: White
• Type: Powder Coating Resins
• Application: Powder Coating
• Characteristic: Good Adhesion,Good Weather Resistance
• Tg: Greater Than or Equal to 64
• Acid Value: 30-35mgkoh/G
• Viscosity: 4000-5000cps
• Curing Conditions: 200ºC/10min
• Product Appearance: White Particles
• Transport Package: PE Bag
• Specification: 25KG/Bag
• Trademark: AquaCity
• Origin: China
• Production Capacity: 15000tons/Year
• Package Size: 53.00cm * 39.00cm * 14.00cm
• Package Gross Weight: 25.000kg

Product Description

 

Curing Agent	Triglycidyl Isocyanurate(TGIC)
	Hydroxy alkyl amide(HAA)
Type of Resins		Item No.	Ratio PE/Crosslinker	Acid Value (mgKOH/g)	Viscosity(p/200ºC) /mpa.s	Tg Value (°C)	Cure cycle ºC/min	Key Features
TGIC Based Polyester Resins		J902	93/7	30~35	4000~5000	≥64	200*10	High gloss ,Excellent flow, weathering resistance and mechanical properties
		J903	93/7	30~35	4500~5500	≥62	200*10	Super weathering resistance, Excellent mechanical properties,good flow
		J906	93/7	30~35	4000~5000	≥65	200*10	High gloss ,Excellent flow, boiling water resistance, mechanical properties
		J907	93/7	29~35	5000~6000	≥67	200*10	Good weathering resistance and mechanical properties,,suitable for texture powder coating
		J801	96/4	18~24	5500~6500	≥65	200*10	For dry blend matte system as fast component,good storage stability
		J802	93/7	30~36	3800~4800	≥65	200*10	Excellent flow,suitable for High gloss and matt
		J808	90/10	48~55	2800~3800	≥66	200*10	For dry blend matte system as fast component,good storage stability
		J301	96/4	18~24	5000~6000	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
		J303	93/7	30~36	3600~4600	≥64	200*10	Low cost resin,good flow and mechanical properties
		J307	93/7	30~35	4800~6000	≥65	200*10	Low cost resin,suitable for texture powder coating
		J308	90/10	50~55	2600~3600	≥65	200*10	Low cost resin,for dry blend matte system as fast component,good storage stability
Primid(HAA) Based Polyester Resins		H602	95/5	20~25	4000~5000	≥64	180*15	Low cost resin,good flow and mechanical properties
		H604	96.5/3.5	18~24	6000~7500	≥61	180*15 200*10	Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing

 
                                                           PRODUCT  PARAMETERS

Product Name			Powder Coating Polyester Resin
Product Model			J902
Product Description			J902 is a special carboxyl terminated polyester resin for 93/7, TGIC curing powder coatings cured at 200 ºC. J902 resin is used for outdoor decorative powder coating,include Great weathering resistance,Excellent leveling surface,Good machanical impact testing results ,Excellent outdoor durability,Apply to Matte surface effects.
Product appearance			White particles
Viscosity (200 ° C,mpa.s)			4000~5000
Acid Value(mgKOH/g)			30-35
Glass Transition  Temperature			≥64
Curing Ratio			93/7

                                            EXTRUSION AND  APPLICATION CONDITIONS

Squeeze
Screw			40HZ
Zone 1 temperature			100
Zone 2  temperature			110
Application
Film thickness, substrate			60-80um film thickness, 0.5mm cold rolled steel plate
Gloss			≥90%
Recoil(kg.cm)			50
Foreflush(kg.cm)			50
Adhesion(grade)			0

Foshan Faxus New Material Company Limited

Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 

• Storage temperature ≤ 30ºC;
• Storage condition is required to be dry and with good air circulation.
• Avoiding sunlight exposure.

PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.